flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	V-2
Burning wire flammability index	Burning wire flammability index	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature	IEC 60695-2-13	775 °C

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.5mm

UL 94

V-2

Burning wire flammability index

IEC 60695-2-12

960 °C

Hot filament ignition temperature

IEC 60695-2-13

775 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Yield,3.17mm	ASTM D790	86.2 MPa
Bending modulus	Bending modulus 3.17mm	ASTM D790	2070 MPa
elongation	elongation Break,3.17mm	ASTM D638	110 %
tensile strength	tensile strength Yield,3.17mm	ASTM D638	55.2 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
RTI Elec	RTI Elec	UL 746	125 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to95°C	ASTME831	6.8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to95°C	ASTME831	7E-05 cm/cm/°C
RTI	RTI	UL 746	125 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	137 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	127 °C
RTI Imp	RTI Imp	UL 746	115 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.20 g/cm³
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ASTM D1238	10 g/10min
Water absorption rate	Water absorption rate 23°C,24hr	ASTM D570	0.15 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

ASTM D792

1.20 g/cm³

melt mass-flow rate

300°C/1.2kg

ASTM D1238

10 g/10min

Water absorption rate

23°C,24hr

ASTM D570

0.15 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot wire ignition	Hot wire ignition 3.0mm	UL 746	PLC 2
	Hot wire ignition	Hot wire ignition 1.5mm	UL 746	PLC 3
		Hot wire ignition	Hot wire ignition 3.00mm	UL 746	PLC 1 sec
		Hot wire ignition	Hot wire ignition	Hot wire ignition 1.50mm	UL 746	PLC 2 sec
High voltage arc tracing rate	High voltage arc tracing rate HVTR	UL 746	PLC 3
High voltage arc tracing rate	High voltage arc tracing rate	High voltage arc tracing rate HVTR	UL 746	PLC 4 mm/min
High arc combustion index	High arc combustion index 3.0mm	UL 746	PLC 1
	High arc combustion index	High arc combustion index 1.5mm	UL 746	PLC 0
		High arc combustion index	High arc combustion index 3.00mm	UL 746	PLC 0
		High arc combustion index	High arc combustion index	High arc combustion index 1.50mm	UL 746	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 2
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 1
Arc resistance	Arc resistance	ASTM D495	PLC6
Arc resistance	Arc resistance	Arc resistance	ASTM D495	60.0to120 sec

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	120

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

120

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.