MF MELOPAS® MF 2500 RASCHIG GmbH

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch Injection	ISO 179/1eU	8.0to13 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch Compression Molded	ISO 179/1eU	7.0to10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength Injection	ISO 179/1eA	1.3to1.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength Compression Molded	ISO 179/1eA	1.3to1.5 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	V-0
Burning wire flammability index	Burning wire flammability index	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature	IEC 60695-2-13	900 °C

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

0.8mm

UL 94

V-0

Burning wire flammability index

IEC 60695-2-12

960 °C

Hot filament ignition temperature

IEC 60695-2-13

900 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus Injection	ISO 178	5000to8000 MPa
tensile strength	tensile strength Injection	ISO 527-2	70.0to90.0 MPa
Compressive stress	Compressive stress	ISO 604	200to250 MPa
bending strength	bending strength Injection	ISO 178	110to140 MPa
bending strength	bending strength	bending strength Compression Molded	ISO 178	100to130 MPa
Tensile modulus	Tensile modulus Compression Molded	ISO 527-2	5000to8000 MPa
Tensile modulus	Tensile modulus	Tensile modulus Injection	ISO 527-2	5000to8000 MPa
tensile strength	tensile strength CompressionMolded	ISO 527-2	40.0to65.0 MPa
Bending modulus	Bending modulus Compression Molded	ISO 178	5000to8000 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Maximum operating temperature	Maximum operating temperature 20,000h	IEC 60216	135 °C
Maximum operating temperature	Maximum operating temperature	Maximum operating temperature <50h	IEC 60216	160 °C
thermal conductivity	thermal conductivity	ASTME1461	0.40to0.50 W/m/K
Hot deformation temperature	Hot deformation temperature 8.0MPa,Unannealed	ISO 75-2/C	120to140 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	170to190 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：50to100°C	ISO 11359-2	1.5E-5到3.5E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Apparent density	Apparent density	ISO 60	0.55to0.75 g/cm³
Shrinkage rate	Shrinkage rate MD：--2	ISO 2577	0.80to1.3 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD：--3	ISO 2577	0.50to1.0 %
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	<2.5 %
density	density	ISO 1183	1.60to1.75 g/cm³
Shrinkage rate	Shrinkage rate	ISO 2577	1.2to2.0 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.030to0.050
Volume resistivity	Volume resistivity	IEC 60093	1.0E+11到1.0E+12 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	1.0E+10到1.0E+11 ohms
Dissipation factor	Dissipation factor 100Hz	IEC 60250	0.30to0.50
Relative permittivity	Relative permittivity 1MHz	IEC 60250	7.009.00
Relative permittivity	Relative permittivity	Relative permittivity 100Hz	IEC 60250	11.016.0
Dielectric strength	Dielectric strength	IEC 60243-1	20to30 kV/mm
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 0
Arc resistance	Arc resistance	ASTM D495	PLC 5

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compression molding pressure	Compression molding pressure		>20.0 MPa
Compression molding temperature	Compression molding temperature		160to180 °C

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Compression molding pressure

>20.0 MPa

Compression molding temperature

160to180 °C

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.