ASA+PA SCHULABLEND® (ASA/PA) M/MW A SCHULMAN USA

So sánh

Bảng thông số kỹ thuật

	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183/A	1.12 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 250°C/5.0kg	ISO 1133	15.0 cm³/10min
Tensile modulus	Tensile modulus	ISO 527-2/1A/1	2000 MPa
tensile strength	tensile strength Yield	ISO 527-2/1A/50	55.0 MPa
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	15 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	77 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NoBreak
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/Bf	116 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	142 °C
Burning rate	Burning rate	ISO 3795	<100 mm/min
UL flame retardant rating	UL flame retardant rating 1.6mm	IEC 60695-11-10,-20	HB
Tensile strain	Tensile strain Yield	ISO 527-2/1A/50	4.0 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.