PCT Infino TK-2050HL LOTTE KOREA

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.35mm	ASTM D256	200 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.18mm	ASTM D256	250 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	3.6 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.35mm	ASTM D256	27 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -5°C	ISO 180/1U	16 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	20 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	22 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.18mm	ASTM D256	29 J/m

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.530mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.530mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break	ASTM D638	2.1 %
tensile strength	tensile strength Break	ISO 527-2/5	56.0 MPa
	tensile strength	tensile strength Break	ASTM D638	58.8 MPa
		tensile strength	tensile strength Yield	ISO 527-2/5	56.0 MPa
		tensile strength	tensile strength	tensile strength Yield	ASTM D638	58.8 MPa
Tensile modulus	Tensile modulus	ISO 527-2/5	4100 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	4060 MPa
bending strength	bending strength	ASTM D790	90.2 MPa
bending strength	bending strength	bending strength	ISO 178	80.0 MPa
Tensile strain	Tensile strain Break	ISO 527-2/5	2.1 %
Bending modulus	Bending modulus	ASTM D790	6080 MPa
Bending modulus	Bending modulus	Bending modulus	ISO 178	5200 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,4.00mm	ISO 75-2/B	250 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	202 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,4.00mm	ISO 75-2/A	202 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	250 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ash content	ash content --	ASTM D5630	51 %
ash content	ash content	ash content --	ISO 3451	51 %
Shrinkage rate	Shrinkage rate MD:3.20mm	ISO 2577	0.54 %
	Shrinkage rate	Shrinkage rate TD:3.20mm	ISO 2577	0.56 %
		Shrinkage rate	Shrinkage rate TD：3.20mm	ASTM D955	0.56 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD：3.20mm	ASTM D955	0.54 %
melt mass-flow rate	melt mass-flow rate 300°C/2.16kg	ISO 1133	15 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 300°C/2.16kg	ASTM D1238	15 g/10min
density	density	ISO 1183	1.77 g/cm³
density	density	density	ASTM D792	1.77 g/cm³

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ISO 2039-2	111
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	111

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ISO 2039-2

111

Rockwell hardness

R-Scale

ASTM D785

111

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.