Unspecified ED223AE Borealis AG

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	6.5 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength -20°C	ISO 179/1eA	11 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	70 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -20°C	ISO 179/1eU	220 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C	ISO 180/1A	13 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	57 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1	1300 MPa
tensile strength	tensile strength Yield	ISO 527-2/50	16.0 MPa
Tensile strain	Tensile strain Yield	ISO 527-2/50	7.0 %
Tensile strain	Tensile strain	Tensile strain Break	ISO 527-2/50	>200 %
Bending modulus	Bending modulus	ISO 178	1350 MPa
bending strength	bending strength	ISO 178	21.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	121 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	38.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to80°C	Internal Method	5.1E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	89.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	49.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.01 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	9.0 g/10min
Shrinkage rate	Shrinkage rate --2	Internal Method	0.80 %
Shrinkage rate	Shrinkage rate	Shrinkage rate 90°C,2hr	Internal Method	0.10 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test H132/10	ISO 2039-1	31.0 MPa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

H132/10

ISO 2039-1

31.0 MPa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.