LLDPE DOWLEX™ 2045G DOW SPAIN

317

Đặc tính:
Sức mạnh cao
Lĩnh vực ứng dụng:
phim
So sánh

Bảng thông số kỹ thuật

optical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
gloss	gloss 45°，50.8um	ASTM D-2457	60
turbidity	turbidity 50.8um	ASTM D-1003	10 %
gloss	gloss	ASTM2457	60
turbidity	turbidity	ASTM D1003	10 %

Other performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Thin film puncture strength	Thin film puncture strength 50.8um	Internal Method	19.4 J/cm³
Film toughness	Film toughness 50.8um，MD	ASTM D-882	346 J/cm³
Film toughness	Film toughness	Film toughness 50.8um，TD	ASTM D-882	351 J/cm4
Elmendorf tear strength	Elmendorf tear strength	ASTM D1922	17.8 g/micron
Elmendorf tear strength	Elmendorf tear strength	Elmendorf tear strength	ASTM D1922	23.6 g/micron
impact force	impact force	ASTM D882	4176 ft-lbf/in3
impact force	impact force	impact force	ASTM D882	4241 ft-lbf/in3

machinability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melt Temperature	Melt Temperature		232 °C

machinability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Melt Temperature

232 °C

Basic Performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D-792	0.92 g/m3
melt mass-flow rate	melt mass-flow rate 190℃/2.16kg	ASTM D-1238	1 g/10min
film thickness	film thickness		50.8 um

Basic Performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

ASTM D-792

0.92 g/m3

melt mass-flow rate

190℃/2.16kg

ASTM D-1238

1 g/10min

film thickness

50.8 um

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Secant modulus	Secant modulus 2% Secant，50.8um，MD	ASTM D-882	194 Mpa
Secant modulus	Secant modulus	Secant modulus 2% Secant，50.8um，TD	ASTM D-882	233 Mpa
tensile strength	tensile strength 50.8um，Yield,MD	ASTM D-882	10.9 Mpa
	tensile strength	tensile strength 50.8um，Yield,TD	ASTM D-882	12.3 Mpa
		tensile strength	tensile strength 50.8um，TD,Break	ASTM D-882	55.1 Mpa
		tensile strength	tensile strength	tensile strength 50.8um，MD,Break	ASTM D-882	49.8 Mpa
Elongation at Break	Elongation at Break 50.8um，TD	ASTM D-882	890 %
Elongation at Break	Elongation at Break	Elongation at Break 50.8um，MD	ASTM D-882	830 %
impact force	impact force		235 ft-lbf/in3
elongation	elongation Break	ASTM D882	827 %
elongation	elongation	elongation Break	ASTM D882	889 %
Elmendorf tear strength	Elmendorf tear strength	ASTM D192	902 g
Elmendorf tear strength	Elmendorf tear strength	Elmendorf tear strength	ASTM D192	1200 g
Dart impact	Dart impact	ASTM D1709	288 g
tensile strength	tensile strength	ASTM D882	10.89 Mpa
tensile strength	tensile strength	tensile strength	ASTM D882	12.29 Mpa
Secant modulus	Secant modulus	ASTM D882	194.4 Mpa
Secant modulus	Secant modulus	Secant modulus	ASTM D882	232.6 Mpa
tensile strength	tensile strength	ASTM D882	55.11 Mpa
tensile strength	tensile strength	tensile strength	ASTM D882	49.81 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature	ASTM D-1525	108 °C
Melting temperature	Melting temperature	Internal Method	122 °C
Vicat softening temperature	Vicat softening temperature	ASTM1525	108 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature Melting Temperature	陶氏化学方法(DSC	122 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate ℃/Kg	ASTM D1238	1.0 g/10min
melt mass-flow rate	melt mass-flow rate 厚度		50.8 microns

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

melt mass-flow rate

℃/Kg

ASTM D1238

1.0 g/10min

melt mass-flow rate

厚度

50.8 microns

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.