PPO NORYL™ FE1520PW-73701 SABIC EU

Đặc tính:
Hấp thụ nước thấp
Chống nước nóng
Lĩnh vực ứng dụng:
Việt
Vòi nước
Cánh quạt bơm nước
Vòi hoa
So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	30 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	4.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	6.0 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	23 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	25 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	7110 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	7180 Mpa
tensile strength	tensile strength Break	ASTM D638	119 Mpa
tensile strength	tensile strength	tensile strength Break	ISO 527-2/5	119 Mpa
elongation	elongation Break	ASTM D638	2.6 %
Tensile strain	Tensile strain Break	ISO 527-2/5	2.6 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	6970 Mpa
Bending modulus	Bending modulus	Bending modulus	ISO 178	6040 Mpa
bending strength	bending strength	ISO 178	165 Mpa
bending strength	bending strength	bending strength Break,50.0mmSpan	ASTM D790	175 Mpa
Taber abraser	Taber abraser 1000Cycles,1000g,CS-17Wheel	Internal Method	65.0 mg

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	139 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	135 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	132 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	150 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	144 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	7E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/10.0kg	ISO 1133	22.0 cm3/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.20-0.40 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD：3.20mm	Internal Method	0.30-0.60 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,50%RH	ASTM D570	0.060 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test H358/30	ISO 2039-1	220 Mpa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

H358/30

ISO 2039-1

220 Mpa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.