PC+ABS TAROBLEND 85 X0 Taro Plast S.p.A.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	20 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	无断裂
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTMD256	500 J/m

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Charpy Notched Impact Strength

23°C

ISO 179

20 kJ/m²

Impact strength of simply supported beam without notch

23°C

ISO 179

无断裂

Impact strength of cantilever beam gap

ASTMD256

500 J/m

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.7mm	UL 94	V-0
Hot filament ignition temperature	Hot filament ignition temperature	IEC 60695-2-13	960 °C

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.7mm

UL 94

V-0

Hot filament ignition temperature

IEC 60695-2-13

960 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield	ASTMD638	50.0 MPa
Bending modulus	Bending modulus	ASTMD790	2100 MPa
bending strength	bending strength --3	ISO 178	70.0 MPa
bending strength	bending strength	bending strength Yield	ASTM D790	70.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTMD648	110 °C
Vicat softening temperature	Vicat softening temperature --	ASTMD15255	135 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ASTMD15256	125 °C
Ball Pressure Test	Ball Pressure Test 125°C	VDE0470	通过

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTMD792	1.20 g/cm³
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.40to0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ASTM D955	0.40to0.70 %
Water absorption rate	Water absorption rate 23°C,24hr	ASTMD570	0.10 %
	Water absorption rate	Water absorption rate Saturation	ASTM D570	0.40 %
	Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.40 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 3

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Compared to the anti leakage trace index

SolutionA

IEC 60112

PLC 3

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.