Basic Performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220℃,10kg	ISO 1133	7.20 cm
melt mass-flow rate	melt mass-flow rate 230℃,3.8kg	ASTM D-1238	2.0 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 220℃,10kg	ASTM D-1238	7.0 g/10min
density	density	ISO 1183	1.06

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃,12.7mm	ASTM D-256	112 J/m
Bending modulus	Bending modulus 23℃	ASTM D-790	2210 MPa
elongation	elongation Break	ASTM D-638	35 %
tensile strength	tensile strength Yield,23℃	ASTM D-638	42.1 MPa
Tensile modulus	Tensile modulus 23℃	ISO 527-1	2500 MPa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃,6.35mm	ASTM D-256	128 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃,3.18mm	ASTM D-256	192 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃	ISO 179/1eU	70.0 KJ/m
	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30℃	ISO 179/1eA	5.90 KJ/m
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃	ISO 179/1eA	11.0 KJ/m
bending strength	bending strength 23℃，Yield	ASTM D-790	69.6 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Combustibility	Combustibility 1.60mm	UL 94	HB
Hot deformation temperature	Hot deformation temperature 0.45MPa，Unannealed，3.18mm	ASTM D-648	101 ℃
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa	ISO 75-1	101 ℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	ASTM D-696	0.000079 cm/cm℃
Vicat softening temperature	Vicat softening temperature Rate B,Loading 1(10N)	ASTM D-1525	117 ℃
Hot deformation temperature	Hot deformation temperature 1.80MPa，Unannealed，12.7mm	ASTM D-648	100 ℃
	Hot deformation temperature	Hot deformation temperature 1.80MPa，Unannealed，6.35mm	ASTM D-648	97.2 ℃
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.80MPa，Unannealed，3.18mm	ASTM D-648	86.1 ℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate	ASTM D-955	0.40-0.70 %
density	density	ASTM D-792	1.05

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

ASTM D-955

0.40-0.70 %

density

ASTM D-792

1.05

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohm.cm
Surface resistivity	Surface resistivity	IEC 60093	1E+15 ohms

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

IEC 60093

1E+15 ohm.cm

Surface resistivity

IEC 60093

1E+15 ohms

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.