TPO PRE-ELEC® PP 1351 Premix Oy
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180 | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -20°C,4.00mm | ASTM D256 | 21.0 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C,4.00mm | ASTM D256 | NoBreak |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -20°C | ISO 180 | 20 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ISO 180 | NoBreak |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -20°C | ASTM D256 | 2.1 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -20°C | ISO 179 | 2.0 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179 | 9.0 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ASTM D256 | 8.4 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -20°C | ASTM D256 | 32 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -20°C | ISO 179 | 32 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179 | NoBreak |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ASTM D256 | NoBreak |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -20°C,4.00mm，Area | ASTM D256 | 2.10 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C,4.00mm，Area | ASTM D256 | 8.41 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -20°C | ISO 180 | 3.0 kJ/m² |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile strain | Tensile strain Yield | ISO 527-2 | 6.0 % |
| Tensile strain | Tensile strain Break,4.00mm | ISO 527-2 | 10 % |
| Bending modulus | Bending modulus 4.00mm | ASTM D790 | 1380 MPa |
| Bending modulus | Bending modulus 4.00mm | ISO 178 | 1400 MPa |
| tensile strength | tensile strength | ASTM D638 | 22.0 MPa |
| tensile strength | tensile strength Yield | ASTM D638 | 25.0 MPa |
| tensile strength | tensile strength Yield | ISO 527-2 | 25.0 MPa |
| tensile strength | tensile strength 4.00mm | ISO 527-2 | 22.0 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/A50 | 148 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 82.0 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ASTM D648B | 83.9 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/Bf | 84.0 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ASTM D648A | 47.8 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/Af | 48.0 °C |
| Vicat softening temperature | Vicat softening temperature -- | ASTM D15253 | 148 °C |
| Vicat softening temperature | Vicat softening temperature -- | ASTM D15254 | 82.2 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density | ASTM D792 | 0.996 g/cm³ |
| density | density | ISO 1183 | 0.990 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 230°C/2.16kg | ISO 1133 | 6.0 g/10min |
| melt mass-flow rate | melt mass-flow rate 230°C/5.0kg | ISO 1133 | 28 g/10min |
| Shrinkage rate | Shrinkage rate MD | ASTM D955 | 1.2to1.8 % |
| Shrinkage rate | Shrinkage rate MD | ISO 294-4 | 1.2to1.8 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Surface resistivity | Surface resistivity | IEC 61340-2-3 | 1.0E+5to1.0E+8 ohms |
| Volume resistivity | Volume resistivity | Internal Method | 1.0E+3to1.0E+7 ohms·cm |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shore hardness | Shore hardness ShoreA | ASTM D2240 | 98 |
| Shore hardness | Shore hardness ShoreD | ASTM D2240 | 74 |
| Shore hardness | Shore hardness ShoreA | ISO 868 | 98 |
| Shore hardness | Shore hardness ShoreD | ISO 868 | 74 |