PA66 ECOMID® ARX H GF40 Celanese Corporation

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	6.5 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating 0.40mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus 23°C	ISO 527-2	10000 MPa
tensile strength	tensile strength Yield,23°C	ISO 527-2	140 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2	2.5 %

mechanical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Tensile modulus

23°C

ISO 527-2

10000 MPa

tensile strength

Yield,23°C

ISO 527-2

140 MPa

Tensile strain

Break,23°C

ISO 527-2

2.5 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	250 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	230 °C
Continuous use temperature	Continuous use temperature	IEC 60216	120 °C
Ball Pressure Test	Ball Pressure Test 125°C	IEC 60695-10-2	通过
Ball Pressure Test	Ball Pressure Test	Ball Pressure Test 165°C	IEC 60695-10-2	通过

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.42 g/cm³
Shrinkage rate	Shrinkage rate TD:23°C	ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD:23°C	ISO 294-4	0.40 %
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	1.7 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	4.5 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohms·cm

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

IEC 60093

1E+15 ohms·cm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.