flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.40 mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating 0.75 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating 2.5 mm	UL 94	5VA

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

0.40 mm

UL 94

V-2

UL flame retardant rating

0.75 mm

UL 94

V-0

UL flame retardant rating

2.5 mm

UL 94

5VA

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength --2,3	ISO 178	108 Mpa
bending strength	bending strength	bending strength --	ASTM D790	99.0 Mpa
Bending modulus	Bending modulus --2	ISO 178	2600 Mpa
Bending modulus	Bending modulus	Bending modulus --	ASTM D790	2350 Mpa
Tensile strain	Tensile strain Break	ISO 527-2/50	4.5 %
Tensile strain	Tensile strain	Tensile strain Break	Internal Method	85 %
tensile strength	tensile strength Yield	ISO 527-2/50	73.0 Mpa
tensile strength	tensile strength	tensile strength Yield	Internal Method	63.0 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	105 to 110 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Suggested injection volume	Suggested injection volume	30 to 70 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	245 to 295 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	255 to 300 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	265 to 305 °C
Spray nozzle temperature	Spray nozzle temperature	275 to 305 °C
Processing (melt) temperature	Processing (melt) temperature	275 to 305 °C
Mold temperature	Mold temperature	70 to 100 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	20 to 100 rpm
Exhaust hole depth	Exhaust hole depth	0.038 to 0.051 mm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40°C	ISO 11359-2	7.6E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ISO 11359-2	6.6E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -30 to 30°C	TMA	7.0E-5 cm/cm/°C
Ball Pressure Test	Ball Pressure Test 125°C	IEC 60695-10-2	通过
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	142 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/A120	151 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span5	ISO 75-2/Af	117 °C
	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm	ASTM D648	125 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 6.40 mm	ASTM D648	136 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 250°C/10.0 kg	ASTM D1238	3.9 g/10 min
Water absorption rate	Water absorption rate 24 hr	ASTM D570	0.070 %
Shrinkage rate	Shrinkage rate 3.20 mm，Flow	Internal Method	0.50 - 0.70 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/5.0 kg	ISO 1133	23.0 cm3/10min
	Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/5.0 kg	ISO 1133	10.0 cm3/10min
	Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/10.0 kg	ISO 1133	27.0 cm3/10min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dielectric constant	Dielectric constant 60 Hz	ASTM D150	2.80
Dielectric constant	Dielectric constant 50 kHz	ASTM D150	2.80
Surface resistivity	Surface resistivity	ASTM D257	1.0E+16 ohms

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Dielectric constant

60 Hz

ASTM D150

2.80

Dielectric constant

50 kHz

ASTM D150

2.80

Surface resistivity

ASTM D257

1.0E+16 ohms

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.

Có thể bạn cũng quan tâm

PPO PX9406P-7001 Nhựa đổi mới cơ bản (Nhật Bản)

$4,242/MT

PPO PX9406P-7001 Nhựa đổi mới cơ bản (Nhật Bản)

₫117.240/KG