impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	110 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	90 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	90 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638/ISO 527	11200 kg/cm²(MPa)[Lb/in²]
tensile strength	tensile strength	ASTM D638/ISO 527	174 kg/cm²(MPa)[Lb/in²]
Bending modulus	Bending modulus	ASTM D790/ISO 178	10400 kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	ASTM D790/ISO 178	280 kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	bending strength FlexuralStrainatFlexuralStrength5(23°C)		4.2 %
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	12000 Mpa
tensile strength	tensile strength Break,23°C	ISO 527-2/5	185 Mpa
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	3.4 %
Bending modulus	Bending modulus 23°C	ISO 178/A	11000 Mpa
bending strength	bending strength 3.5%Strain	ISO 178/A	280 Mpa
bending strength	bending strength	bending strength 23°C	ISO 178	290 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Combustibility (rate)	Combustibility (rate)	UL 94	HB
Vicat softening temperature	Vicat softening temperature	ASTM D1525/ISO R306	200 ℃（℉）
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	217 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	201 °C
Melting temperature	Melting temperature	ISO 11357-3	220 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792/ISO 1183	1.46
Shrinkage rate	Shrinkage rate TD:280°C,2.00mm2	ISO 294-4	0.75 %
	Shrinkage rate	Shrinkage rate TD:120°C,2hr,2.00mm3	ISO 294-4	0.090 %
		Shrinkage rate	Shrinkage rate MD:280°C,2.00mm2	ISO 294-4	0.21 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD:120°C,2hr,2.00mm3	ISO 294-4	0.070 %

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ISO Shortcut	ISO Shortcut	ISO 1874	PA6HI.GR.14-120.GF40

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ISO Shortcut

ISO 1874

PA6HI.GR.14-120.GF40

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.