PBT Generic ABS+PBT - Glass Fiber Generic
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179 | 5.9to8.2 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ASTM D256 | 56to83 J/m |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| elongation | elongation Break,23°C | ISO 527-2 | 2.5to3.5 % |
| tensile strength | tensile strength Yield,23°C | ASTM D638 | 67.1to123 MPa |
| tensile strength | tensile strength Yield,23°C | ISO 527-2 | 78.8to120 MPa |
| tensile strength | tensile strength Break,23°C | ASTM D638 | 77.5to112 MPa |
| Bending modulus | Bending modulus 23°C | ASTM D790 | 3180to10300 MPa |
| Bending modulus | Bending modulus 23°C | ISO 178 | 3800to9770 MPa |
| bending strength | bending strength 23°C | ASTM D790 | 86.1to190 MPa |
| bending strength | bending strength 23°C | ISO 178 | 114to171 MPa |
| tensile strength | tensile strength 23°C | ASTM D638 | 77.7to105 MPa |
| elongation | elongation Break,23°C | ASTM D638 | 1.5to4.4 % |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 196to220 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ASTM D648 | 104to202 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 104to191 °C |
| Vicat softening temperature | Vicat softening temperature | ISO 306 | 100to218 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD | ASTM D696 | 2.8E-5到6.6E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD | ISO 11359-2 | 2.0E-5到4.0E-5 cm/cm/°C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ASTM D648 | 198to211 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD | ISO 11359-2 | 7.9E-5到1.0E-4 cm/cm/°C |
| RTI Elec | RTI Elec | UL 746 | 59.0to140 °C |
| RTI Imp | RTI Imp | UL 746 | 58.8to100 °C |
| RTI | RTI | UL 746 | 60.0to130 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density 23°C | ISO 1183 | 1.28to1.61 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 250°C/5.0kg | ASTM D1238 | 14to40 g/10min |
| Shrinkage rate | Shrinkage rate MD：23°C | ASTM D955 | 0.20to0.67 % |
| Water absorption rate | Water absorption rate 23°C,24hr | ASTM D570 | 0.12to0.15 % |
| Water absorption rate | Water absorption rate 23°C,24hr | ISO 62 | 0.15 % |
| density | density -- | ASTM D792 | 1.23to1.55 g/cm³ |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Volume resistivity | Volume resistivity 23°C | ASTM D257 | 1.0E+15到1.0E+17 ohms·cm |
| Volume resistivity | Volume resistivity 23°C | IEC 60093 | 1.0E+15到2.5E+17 ohms·cm |
| Dielectric strength | Dielectric strength 23°C | ASTM D149 | 18to35 kV/mm |
| Arc resistance | Arc resistance | ASTM D495 | 69.0to85.5 sec |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index | IEC 60112 | PLC 0 |
| High arc combustion index | High arc combustion index HAI | UL 746 | PLC 1 |
| High voltage arc tracing rate | High voltage arc tracing rate HVTR | UL 746 | PLC 4 mm/min |
| Hot wire ignition | Hot wire ignition HWI | UL 746 | PLC 2 sec |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Rockwell hardness | Rockwell hardness 23°C | ASTM D785 | 114to120 |