elastomer	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Permanent compression deformation	Permanent compression deformation 70°C,24hr	ISO 815	40 %
	Permanent compression deformation	Permanent compression deformation 23°C,24hr	ISO 815	20 %
		Permanent compression deformation	Permanent compression deformation 70°C,24hr	ASTM D395	40 %
		Permanent compression deformation	Permanent compression deformation	Permanent compression deformation 23°C,24hr	ASTM D395	20 %
tear strength	tear strength	ISO 34-1	40 kN/m
tear strength	tear strength	tear strength	ASTM D624	71.8 kN/m
elongation	elongation Break	DIN 53504	800 %
elongation	elongation	elongation Break	ASTM D412	800 %
tensile strength	tensile strength Break	DIN 53504	30.0 Mpa
	tensile strength	tensile strength Break	ASTM D412	27.6 Mpa
		tensile strength	tensile strength 300%Strain	DIN 53504	8.00 Mpa
			tensile strength	tensile strength 300%Strain	ASTM D412	9.65 Mpa
				tensile strength	tensile strength 100%Strain	DIN 53504	5.20 Mpa
				tensile strength	tensile strength	tensile strength 100%Strain	ASTM D412	5.79 Mpa

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength	DIN 53504	34 Mpa
Tensile modulus	Tensile modulus 100%	DIN 53504	4.0 Mpa
Wear resistance	Wear resistance	ISO 4649	40 mm³
Tensile modulus	Tensile modulus 300%	DIN 53504	7.0 Mpa
elongation	elongation Break	DIN 53504	670 %
tear strength	tear strength	ISO 34-1	76 N/mm
Wear resistance	Wear resistance	ISO 4649	40 mm³
Compression permanent deformation for 24 hours at 23 ℃	Compression permanent deformation for 24 hours at 23 ℃	ISO 815	24 %
Compression permanent deformation for 24 hours at 70 ℃	Compression permanent deformation for 24 hours at 70 ℃	ISO 815	42 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
TMA	TMA Low:635.0μm	Internal Method	165 °C
TMA	TMA	TMA High:635.0μm	Internal Method	190 °C
Melting temperature	Melting temperature 下限	Huntsman	127 °C
Melting temperature	Melting temperature	Melting temperature	Huntsman	156 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness	ISO 7619	80 Shore A
Shore hardness	Shore hardness	Shore hardness	ISO 7619	31 Shore D
Shrinkage rate	Shrinkage rate MD：Injection	ASTM D955	1.0 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 190°C/21.6kg		110 cm3/10min

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreD,Injection	ISO 868	30
	Shore hardness	Shore hardness ShoreA,Injection	ISO 868	82
		Shore hardness	Shore hardness ShoreD,Injection	ASTM D2240	30
		Shore hardness	Shore hardness	Shore hardness ShoreA,Injection	ASTM D2240	82

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.