Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	12 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of cantilever beam gap

-30°C

ISO 180/1A

10 kJ/m²

Impact strength of cantilever beam gap

23°C

ISO 180/1A

12 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	HB
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	650 °C
UL flame retardant rating	UL flame retardant rating 1.60 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.20 mm	UL 94	HB
Burning wire flammability index	Burning wire flammability index 2.00 mm	IEC 60695-2-12	650 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus 23°C	ISO 527-2/5	8500 MPa
tensile strength	tensile strength Break,23°C	ISO 527-2/5	110 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	2.5 %
Tensile modulus	Tensile modulus 23°C	ISO 527-2/5	8500 MPa
tensile strength	tensile strength Break, 23°C	ISO 527-2/5	110 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	2.5 %
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	12 kJ/m²

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	205 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	195 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B	200 °C
Melting temperature	Melting temperature	ISO 11357	223 °C
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed	ISO 75-2/B	205 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed	ISO 75-2/A	195 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B	200 °C
Melting temperature	Melting temperature	ISO 11357	223 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.33 g/cm³
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.9 %
water content	water content	ISO 960	<2000 ppm
Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	1.9 %
density	density	ISO 1183	1.33 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 1
Surface resistivity	Surface resistivity	IEC 60093	1E+13 ohms
Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	1E+13 ohms
Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohms·cm
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 1

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.