mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation at yield	elongation at yield	ISO 527-1	9 %
tensile strength	tensile strength Yield	ISO 527-1	33 Mpa
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃,Type 1,Edgewise,Notch A	ISO 179	5 kj/cm
Bending modulus	Bending modulus	ISO 527-1	1450 Mpa
elongation	elongation Break	ISO 527-1	>50 %
Ball Pressure Test	Ball Pressure Test H 358/30	ISO 2039-1	72 Mpa
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23℃,Type 1,Edgewise	ISO 179	No Break kj/cm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature B50(50℃/h 50N)	ISO 306	90 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa Unannealed	ISO 75B-1	85 °C
Vicat softening temperature	Vicat softening temperature A50(50℃/h 10N)	ISO 306	154 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Vicat softening temperature

B50(50℃/h 50N)

ISO 306

90 °C

Hot deformation temperature

0.45MPa Unannealed

ISO 75B-1

85 °C

Vicat softening temperature

A50(50℃/h 10N)

ISO 306

154 °C

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.