PPO(PPE)+PS+PA NORYL GTX™ GTX840 resin SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/2C	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C7	ISO 179/1eA	11 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	90 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	94 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C8	ISO 180/1A	11 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C8	ISO 180/1A	11 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus --2	ASTM D638	13500 MPa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	13900 MPa
tensile strength	tensile strength Break3	ASTM D638	178 MPa
tensile strength	tensile strength	tensile strength Break	ISO 527-2/5	198 MPa
elongation	elongation Break3	ASTM D638	2.0 %
elongation	elongation	elongation Break	ISO 527-2/5	2.0 %
Bending modulus	Bending modulus 50.0mmSpan4	ASTM D790	11900 MPa
Bending modulus	Bending modulus	Bending modulus --5	ISO 178	12300 MPa
bending strength	bending strength --5,6	ISO 178	280 MPa
bending strength	bending strength	bending strength Yield,50.0mmSpan4	ASTM D790	249 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan9	ISO 75-2/Bf	258 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	247 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan9	ISO 75-2/Af	244 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	246 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to40°C	ASTME831	1.6E-5到2.0E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to40°C	ASTME831	9.0E-5到9.4E-5 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	260 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C	ASTM D570	0.30 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.10 %
density	density	ASTMD792	1.45 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220°C/5.0kg	ISO 1133	10.0 cm³/10min
Shrinkage rate	Shrinkage rate MD:3.20mm	Internal Method	0.24to0.27 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD:3.20mm	Internal Method	0.60to0.63 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	108

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

108

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.