mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D-638	1830 MPa
tensile strength	tensile strength Yield	ASTM D-638	21.0 MPa
tensile strength	tensile strength	tensile strength Break	ASTM D-638	18.0 MPa
Elongation at Break	Elongation at Break	ASTM D-638	55 %
Bending modulus	Bending modulus 23℃	ASTM D-790	2090 MPa
bending strength	bending strength	ASTM D-790	44.0 MPa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -18℃,3.18mm	ASTM D-256	85.0 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃,3.20mm	ASTM D-256	224 J/m

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa，Unannealed	ASTM D-648	84.0 ℃
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.80MPa，Unannealed	ASTM D-648	71.0 ℃
Vicat softening temperature	Vicat softening temperature Rate B,120℃/h	ASTM D-1525	101 ℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ASTM D-696	0.000081 cm/cm℃
Combustibility	Combustibility	UL 94	HB

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D-792	1.03
Shrinkage rate	Shrinkage rate Flow	ASTM D-955	0.30-0.70 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

ASTM D-792

1.03

Shrinkage rate

Flow

ASTM D-955

0.30-0.70 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.