PP LNP™ THERMOTUF™ MF004AI compound SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	170 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	14 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D4812	440 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	28 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Break	ASTM D638	40.0 MPa
tensile strength	tensile strength	tensile strength Break	ISO 527-2	37.0 MPa
bending strength	bending strength	ISO 178	46.0 MPa
Tensile modulus	Tensile modulus	ASTM D638	4830 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	4940 MPa
elongation	elongation Break	ASTM D638	4.8 %
Tensile strain	Tensile strain Break	ISO 527-2	4.5 %
Bending modulus	Bending modulus	ASTM D790	2760 MPa
Bending modulus	Bending modulus	Bending modulus	ISO 178	3000 MPa
bending strength	bending strength	ASTM D790	41.4 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	151 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	144 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	109 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	104 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	1.1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	1.1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	6.8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	6.8E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD:24hr	ISO 294-4	1.2 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD:24hr	ISO 294-4	1.2 %
density	density	ASTM D792	1.03 g/cm³
density	density	density	ISO 1183	1.03 g/cm³
Shrinkage rate	Shrinkage rate MD：24hr	ASTM D955	1.1to1.3 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD：24hr	ASTM D955	1.1to1.3 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.