PA66 Durethan® AKV35H2.0 901510 LANXESS GERMANY
- Lĩnh vực ứng dụng:Sản phẩm bànMáy giặtĐồ chơi
- Giấy chứng nhận:UL
So sánh
Xem giáBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ISO 180/1U | 75 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -30°C | ISO 180/1U | 65 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | 85 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | 75 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 1.6mm | UL 94 | HB |
| UL flame retardant rating | UL flame retardant rating 3.2mm | UL 94 | HB |
| Burning wire flammability index | Burning wire flammability index 2.0mm | IEC 60695-2-12 | 650 °C |
| Extreme Oxygen Index | Extreme Oxygen Index | ISO 4589-2 | 26 % |
| BurningBehavior | BurningBehavior >1.00mm | ISO 3795 | passed |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus 23°C | ISO 527-2/1 | 11500 Mpa |
| Tensile modulus | Tensile modulus 23°C | ASTM D638 | 11000 Mpa |
| bending strength | bending strength FlexuralStrainatFlexuralStrength6(23°C) | 3.8 % | |
| bending strength | bending strength 23°C | ISO 178 | 305 Mpa |
| bending strength | bending strength 3.5%Strain | ISO 178/A | -- Mpa |
| bending strength | bending strength 23°C | ASTM D790 | 290 Mpa |
| Bending modulus | Bending modulus 23°C | ISO 178/A | 10700 Mpa |
| Bending modulus | Bending modulus 23°C | ASTM D790 | 10000 Mpa |
| Tensile strain | Tensile strain Break,23°C | ISO 527-2/5 | 3.1 % |
| elongation | elongation Break,23°C | ASTM D638 | 3.0 % |
| tensile strength | tensile strength Break,23°C | ISO 527-2/5 | 195 Mpa |
| tensile strength | tensile strength Break,23°C | ASTM D638 | 190 Mpa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,4.00mm | ASTM D648 | >249 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 250 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,4.00mm | ASTM D648 | >249 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 245 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | >230 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B120 | 255 °C |
| Melting temperature | Melting temperature | ISO 11357-3 | 262 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to55°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：23to55°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 1.7 % |
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 5.2 % |
| Shrinkage rate | Shrinkage rate MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.060 % |
| Shrinkage rate | Shrinkage rate MD:300°C,2.00mm2 | ISO 294-4 | 0.38 % |
| Shrinkage rate | Shrinkage rate TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.090 % |
| Shrinkage rate | Shrinkage rate TD:300°C,2.00mm2 | ISO 294-4 | 1.1 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Surface resistivity | Surface resistivity | IEC 60093 | 1E+14 ohms |
| Volume resistivity | Volume resistivity 23°C | IEC 60093 | 1E+15 ohms·cm |
| Dielectric strength | Dielectric strength 23°C,1.00mm | IEC 60243-1 | 35 KV/mm |
| Dielectric strength | Dielectric strength 23°C,3.00mm | IEC 60243-1 | 40 KV/mm |
| Dielectric constant | Dielectric constant 23°C,50Hz | IEC 60250 | 4.00 |
| Dielectric constant | Dielectric constant 23°C,1MHz | IEC 60250 | 4.00 |
| Relative permittivity | Relative permittivity 23°C,100Hz | IEC 60250 | 3.90 |
| Relative permittivity | Relative permittivity 23°C,1MHz | IEC 60250 | 3.60 |
| Dissipation factor | Dissipation factor 23°C,50Hz | IEC 60250 | 6E-03 |
| Dissipation factor | Dissipation factor 23°C,100Hz | IEC 60250 | 0.010 |
| Dissipation factor | Dissipation factor 23°C,1MHz | IEC 60250 | 4.0E-30.015 |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index SolutionA | IEC 60112 | V |
| Supplementary Information | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| ISO Shortcut | ISO Shortcut | ISO 1874 | PA66.GHRW.14-110.GF30 |