PP GAPEX® RPP20EU63BN USA Fulu
So sánhBảng thông số kỹ thuật
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| tensile strength | tensile strength 23°C | ASTM D638 | 62.10 MPa |
| Elongation at Break | Elongation at Break 23°C | ASTM D638 | 3.00 % |
| bending strength | bending strength 23°C | ASTM D790 | 95.10 MPa |
| Bending modulus | Bending modulus 23°C | ASTM D790 | 4390 MPa |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ASTM D256 | 53 J/m |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ASTM D256 | 310 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23℃ | ASTM D256 | 53 J/m |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 落锤冲击 | 0.26 J | |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23℃ | ASTM D4812 | 310 J/m |
| Dart impact | Dart impact 23℃ | ASTM D5420 | 0.260 J |
| tensile strength | tensile strength 23℃ | ASTM D638 | 62.1 MPa |
| elongation | elongation Break, 23℃ | ASTM D638 | 3.0 % |
| Bending modulus | Bending modulus 1% Secant: 23℃ | ASTM D790 | 4190 MPa |
| Bending modulus | Bending modulus Tangent: 23℃ | ASTM D790 | 4390 MPa |
| bending strength | bending strength 23℃ | ASTM D790 | 95.1 MPa |
| tensile strength | tensile strength 23°C | ASTM D638 | 62.10 MPa |
| Elongation at Break | Elongation at Break 23°C | ASTM D638 | 3.00 % |
| bending strength | bending strength 23°C | ASTM D790 | 95.10 MPa |
| Bending modulus | Bending modulus 23°C | ASTM D790 | 4390 MPa |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ASTM D256 | 53 J/m |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ASTM D256 | 310 J/m |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 落锤冲击 | 0.26 J |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 0.45MPaUnannealed | ASTM D648 | 155 °C |
| Hot deformation temperature | Hot deformation temperature 1.80MPaUnannealed | ASTM D648 | 142 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPaUnannealed | ASTM D648 | 155 °C |
| Hot deformation temperature | Hot deformation temperature 1.80MPaUnannealed | ASTM D648 | 142 °C |
| Hot deformation temperature | Hot deformation temperature 0.45 MPa, Unannealed | ASTM D648 | 155 ℃ |
| Hot deformation temperature | Hot deformation temperature 1.8 MPa, Unannealed | ASTM D648 | 142 ℃ |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density | ASTM D792 | 1.06 g/cm³ |
| Shrinkage rate | Shrinkage rate MD | ASTM D995 | 0.50 % |
| Shrinkage rate | Shrinkage rate TD | ASTM D995 | 1.20 % |
| melt mass-flow rate | melt mass-flow rate 230℃/2.16Kg | ASTM D1238 | 18 g/10min |
| density | density | ASTM D792 | 1.06 g/cm3 |
| density | density | ASTM D792 | 1.06 g/cm³ |
| Shrinkage rate | Shrinkage rate MD | ASTM D995 | 0.50 % |
| Shrinkage rate | Shrinkage rate TD | ASTM D995 | 1.20 % |
| melt mass-flow rate | melt mass-flow rate 230℃/2.16Kg | ASTM D1238 | 18 g/10min |
| melt mass-flow rate | melt mass-flow rate 230℃/2.16 kg | ASTM D1238 | 18 g/10min |
| Shrinkage rate | Shrinkage rate MD | ASTM D955 | 0.5 % |
| Shrinkage rate | Shrinkage rate TD | ASTM D955 | 1.2 % |