impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	200 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	200 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of simply supported beam without notch

23°C

ISO 179/1eU

200 kJ/m²

Impact strength of simply supported beam without notch

-30°C

ISO 179/1eU

200 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Extreme Oxygen Index	Extreme Oxygen Index	ASTM D2863	23 %
Atomization	Atomization F-value (refraction)	ISO 6452	95 %
Atomization	Atomization	Atomization G-value (condensate)	ISO 6452	2.0E-4 g
Emission	Emission	VDA 275	< 8.00 mg/kg

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Poisson's ratio	Poisson's ratio	ISO 527	0.37
Bending modulus	Bending modulus	ISO 178	3000 Mpa
Tensile creep modulus	Tensile creep modulus 1000 hr	ISO 899-1	1500 Mpa
Tensile creep modulus	Tensile creep modulus	Tensile creep modulus 1 hr	ISO 899-1	2800 Mpa
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2	23 %
Tensile strain	Tensile strain Yield	ISO 527-2	12 %
tensile strength	tensile strength Yield	ISO 527-2	71.0 Mpa
Tensile modulus	Tensile modulus	ISO 527-2	3300 Mpa

injection	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature		80 °C
Drying time - hot air dryer	Drying time - hot air dryer		2.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content		0.20 %
Processing (melt) temperature	Processing (melt) temperature		210 to 220 °C
Melt Temperature, Optimum	Melt Temperature, Optimum		215 °C
Mold temperature	Mold temperature		80 to 100 °C
Mold Temperature, Optimum	Mold Temperature, Optimum		90 °C
Maintain pressure	Maintain pressure		80.0 to 100 Mpa
Maintain pressure	Maintain pressure	Maintain pressure Drying Recommended		yes
Hold Pressure Time	Hold Pressure Time		8.00 s/mm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow	ISO 11359-2	1.2E-4 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ISO 11359-2	1.2E-4 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : 23 to 55°C	ASTM E831	1.0E-4 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	178 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	160 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed	ISO 75-2/A	94.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed	ISO 75-2/B	162 °C
Annealing Time - Optional	Annealing Time - Optional		30.0 min/mm
annealing temperature	annealing temperature		160 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation, 23°C, 2.00 mm	ISO 62	1.4 %
Shrinkage rate	Shrinkage rate Flow	ISO 294-4	1.9 %
Shrinkage rate	Shrinkage rate	Shrinkage rate 横向Flow	ISO 294-4	1.9 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 190°C/2.16 kg	ISO 1133	21.0 cm3/10min
melt mass-flow rate	melt mass-flow rate	ISO 1133	25 g/10 min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 62631-3-2	> 1.0E+15 ohms
Volume resistivity	Volume resistivity	IEC 62631-3-1	1.0E+12 ohms·m
Relative permittivity	Relative permittivity 100 Hz	IEC 62631-2-1	3.80
Relative permittivity	Relative permittivity	Relative permittivity 1 MHz	IEC 62631-2-1	3.80
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	V
Hot wire ignition	Hot wire ignition 0.750 mm	UL 746	sec

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R -Sale	ISO 2039-2	120
Rockwell hardness	Rockwell hardness M -Sale	ISO 2039-2	92

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R -Sale

ISO 2039-2

120

Rockwell hardness

M -Sale

ISO 2039-2

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.