PC LEXAN™ EXL4419-739 SABIC INNOVATIVE US

Đặc tính:
Tăng cườngGia cố sợi thủy tinhChịu nhiệt độ thấp
Lĩnh vực ứng dụng:
Lĩnh vực ô tôThiết bị điệnLĩnh vực điện tửLĩnh vực điệnPhụ tùng nội thất ô tôPhụ tùng ô tô bên ngoài
So sánh Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	15 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	25 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	无断裂
Dart impact	Dart impact 23°C, Total Energy	ASTM D3763	40.0 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus --2	ASTM D638	3300 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	3300 Mpa
tensile strength	tensile strength Yield3	ASTM D638	53.0 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/5	55.0 Mpa
		tensile strength	tensile strength Break3	ASTM D638	44.0 Mpa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/5	43.0 Mpa
elongation	elongation Yield3	ASTM D638	4.5 %
	elongation	elongation Yield	ISO 527-2/5	4.5 %
		elongation	elongation Break3	ASTM D638	20 %
		elongation	elongation	elongation Break	ISO 527-2/5	13 %
Bending modulus	Bending modulus 50.0 mm Span4	ASTM D790	3200 Mpa
Bending modulus	Bending modulus	Bending modulus --5	ISO 178	3300 Mpa
bending strength	bending strength --5,6	ISO 178	90.0 Mpa
bending strength	bending strength	bending strength Yield, 50.0 mm Span4	ASTM D790	95.0 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	120 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Suggested injection volume	Suggested injection volume	40 to 60 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	290 to 310 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	300 to 320 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	310 to 330 °C
Spray nozzle temperature	Spray nozzle temperature	305 to 325 °C
Processing (melt) temperature	Processing (melt) temperature	310 to 330 °C
Mold temperature	Mold temperature	80 to 115 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	40 to 70 rpm
Exhaust hole depth	Exhaust hole depth	0.025 to 0.076 mm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	135 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	134 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D152510	145 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	144 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	146 °C
Ball Pressure Test	Ball Pressure Test 73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ASTM E831	4.1E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 40°C	ASTM E831	6.9E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40°C	ISO 11359-2	6.9E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 300°C/1.2 kg	ASTM D1238	11 g/10 min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/1.2 kg	ISO 1133	10.0 cm3/10min
Shrinkage rate	Shrinkage rate 3.20 mm，Flow	Internal Method	0.20 - 0.60 %
Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	0.12 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.46 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	ASTM D257	2.9E+17 ohms
Volume resistivity	Volume resistivity	ASTM D257	1.8E+17 ohms·cm
Dielectric strength	Dielectric strength 1.60 mm, in Oil	ASTM D149	32 KV/mm
Dielectric constant	Dielectric constant 1 MHz	ASTM D150	3.04
Dielectric constant	Dielectric constant	Dielectric constant 1.90 GHz	Internal Method	2.95
Dissipation factor	Dissipation factor 1 MHz	ASTM D150	8.6E-3
Dissipation factor	Dissipation factor	Dissipation factor 1.90 GHz	Internal Method	5.7E-3

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.