	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
density	density	ASTM D792	1.13 g/cm³
UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	HB
Hot filament ignition temperature	Hot filament ignition temperature 2.0mm	IEC 60695-2-12	750 °C
melt mass-flow rate	melt mass-flow rate 260°C/5.0kg	ASTM D1238	25 g/10min
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.50to0.70 %
tensile strength	tensile strength Yield	ASTM D638	58.0 MPa
tensile strength	tensile strength	tensile strength Break	ASTM D638	45.0 MPa
elongation	elongation Break	ASTM D638	>50 %
Bending modulus	Bending modulus	ASTM D790	2400 MPa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	550 J/m
Vicat softening temperature	Vicat softening temperature --	ASTM D15253	135 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ASTM D15254	123 °C

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.