PPO(PPE)+PS+PA NORYL GTX™ GTX964 resin SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	20 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	50 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	20 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	45 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1	2000 MPa
bending strength	bending strength	ISO 178	70.0 MPa
Bending modulus	Bending modulus	ISO 178	1800 MPa
Tensile strain	Tensile strain Break	ISO 527-2/50	50 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-2/50	4.0 %
tensile strength	tensile strength Break	ISO 527-2/50	45.0 MPa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	50.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test 125°C	IEC 60695-10-2	通过
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	180 °C
thermal conductivity	thermal conductivity	ISO 8302	0.23 W/m/K
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:23to60°C	ISO 11359-2	9E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:23to60°C	ISO 11359-2	9E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	175 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	240 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	175 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.2 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	3.5 %
Shrinkage rate	Shrinkage rate MD2	Internal Method	1.4to1.8 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/2.16kg	ISO 1133	7.00 cm³/10min
density	density	ISO 1183	1.08 g/cm³

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test H358/30	ISO 2039-1	80.0 MPa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

H358/30

ISO 2039-1

80.0 MPa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.