mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ASTM D790	112 MPa
Bending modulus	Bending modulus	ASTM D790	3080 MPa
elongation	elongation Break	ASTM D638	6.0 %
tensile strength	tensile strength	ASTM D638	66.0 MPa
Tensile modulus	Tensile modulus	ASTM D638	3390 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	65.0 °C
Glass transition temperature	Glass transition temperature --4	DMA	132 °C
Glass transition temperature	Glass transition temperature	Glass transition temperature --	DMA	62.0 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed4	ASTM D648	110 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	57.0 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed4	ASTM D648	130 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density --3		1.23 g/cm³
density	density --2		1.17 g/cm³

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

--3

1.23 g/cm³

density

--2

1.17 g/cm³

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreD		86

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreD

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.