PA6 Durethan® B30S LANXESS BELGIUM

281

So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30℃-30 °C	ISO 180-1U	200 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃23 °C	ISO 180-1U	N kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30℃-30 °C	ISO 180-1A	<10
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃23 °C	ISO 180-1A	<10
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃23 °C	ISO 179-1eU	N kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30℃-30 °C	ISO 179-1eA	<10 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃23 °C	ISO 179-1eA	<10 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength 3.50% Strain，2 mm/min3.5%，2 mm/min	ISO 178	90 Mpa
Bending strain	Bending strain 2 mm/min2 mm/min	ISO 178	6 %
bending strength	bending strength 2 mm/min2 mm/min	ISO 178	105 Mpa
Bending modulus	Bending modulus 2 mm/mim2 mm/min	ISO 178	2800 Mpa
Tensile stress	Tensile stress 50 mm/min50 mm/min，Yield	ISO 527-1	80 Mpa
Tensile modulus	Tensile modulus 1 mm/min1 mm/min	ISO 527-1	3200 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa0.45 MPa	ISO 75-1/2	172 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa1.80 MPa	ISO 75-1/2	66 °C
Melting temperature	Melting temperature 10℃ / min10 ℃/min	ISO 11357-1	221 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hot deformation temperature

0.45 MPa0.45 MPa

ISO 75-1/2

172 °C

Hot deformation temperature

1.8 MPa1.80 MPa

ISO 75-1/2

66 °C

Melting temperature

10℃ / min10 ℃/min

ISO 11357-1

221 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate 正常，60x60x2; 120 ℃; 4 h正常,60x60x2; 120 °C; 4 h	ISO 2577	0.27 %
	Shrinkage rate	Shrinkage rate 平行，60x60x2; 120 ℃; 4 h平行,60x60x2; 120 °C; 4 h	ISO 2577	0.27 %
		Shrinkage rate	Shrinkage rate 正常，60x60x2，270℃ / WZ 80℃，600 bar正常,60x60x2; 270 °C / WZ 80 °C; 600 bar	ISO 2577	0.91 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD：60x60x2，270℃ / WZ 80℃，600 bar平行,60x60x2; 270 °C / WZ 80 °C; 600 bar	ISO 2577	1.03 %
density	density	ISO 1183	1122 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.