ABS POLYLAC® PA-737 CHI MEI CORPORATION

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	24 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	10 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.40mm	ASTM D256	180 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.20mm	ASTM D256	250 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	25 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.5mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength --6	ISO 178	60.0 MPa
bending strength	bending strength	bending strength --5	ASTM D790	57.9 MPa
Bending modulus	Bending modulus --6	ISO 178	1900 MPa
Bending modulus	Bending modulus	Bending modulus --5	ASTM D790	1930 MPa
elongation	elongation Break	ISO 527-2/50	20 %
elongation	elongation	elongation Break4	ASTM D638	22 %
tensile strength	tensile strength Break	ISO 527-2/50	32.0 MPa
	tensile strength	tensile strength Yield	ISO 527-2/50	39.0 MPa
	tensile strength	tensile strength	tensile strength Yield4	ASTM D638	35.2 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	9E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	96.0 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	103 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ASTM D15257	101 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ASTM D648	93.0 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	81.0 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	83.0 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	96.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density 23°C	ISO 1183	1.04 g/cm³
density	density	density --3	ASTM D792	1.04 g/cm³
melt mass-flow rate	melt mass-flow rate 200°C/5.0kg	ASTM D1238	2.6 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220°C/10.0kg	ISO 1133	29.0 cm³/10min
Shrinkage rate	Shrinkage rate	ISO 294-4	0.40to0.70 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	103

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

103

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.