thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	179 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	56.1 °C
Hot deformation temperature	Hot deformation temperature Melting Temperature	ASTM D648	210 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hot deformation temperature

0.45MPa,Unannealed

ASTM D648

179 °C

Hot deformation temperature

1.8MPa,Unannealed

ASTM D648

56.1 °C

Hot deformation temperature

Melting Temperature

ASTM D648

210 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.13 g/cm³
Shrinkage rate	Shrinkage rate MD	ASTM D955	1.2 %
Water absorption rate	Water absorption rate 24hr	ASTM D570	1.6 %
	Water absorption rate	Water absorption rate Saturation	ASTM D570	9.6 %
	Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ASTM D570	2.8 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	118

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

118

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.