PA66 Vydyne® R228 Ascend Performance Materials Operations LLC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	7.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	110 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	140 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180	7.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180	9.0 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Poisson's ratio	Poisson's ratio	ISO 527	0.40
Tensile strain	Tensile strain Break,23°C	ISO 527-2	6.0 %
Bending modulus	Bending modulus 23°C	ISO 178	6100 MPa
bending strength	bending strength 23°C	ISO 178	124 MPa
Tensile modulus	Tensile modulus 23°C	ISO 527-2	6900 MPa
tensile strength	tensile strength Yield,23°C	ISO 527-2	103 MPa
Tensile strain	Tensile strain Yield,23°C	ISO 527-2	1.5 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	222 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	118 °C
Melting temperature	Melting temperature	ISO 11357-3	258 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C,2.00mm	ISO 11359-2	6.3E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to55°C,2.00mm	ISO 11359-2	6E-04 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.48 g/cm³
Shrinkage rate	Shrinkage rate TD:23°C,2.00mm	ISO 294-4	1.0 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD:23°C,2.00mm	ISO 294-4	1.1 %
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	1.1 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.6 %

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Automotive Materials	Automotive Materials thicknessd=1mm	FMVSS302	+

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Automotive Materials

thicknessd=1mm

FMVSS302

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.