impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	57 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	600 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	11 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	53 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D4812	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	NoBreak
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	120 J
Dart impact	Dart impact	Dart impact 23°C	ASTM D3029	149 J
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	13 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTM D1822	577 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Yield	ISO 527-2/50	7.0 %
elongation	elongation Break	ASTM D638	>110 %
Tensile strain	Tensile strain Break	ISO 527-2/50	85 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2200 MPa
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	95.0 MPa
bending strength	bending strength	bending strength	ISO 178	66.0 MPa
Bending modulus	Bending modulus	ISO 178	2120 MPa
elongation	elongation Yield	ASTM D638	7.0 %
tensile strength	tensile strength Break	ISO 527-2/50	60.0 MPa
	tensile strength	tensile strength Break	ASTM D638	70.0 MPa
		tensile strength	tensile strength Yield	ISO 527-2/50	65.0 MPa
		tensile strength	tensile strength	tensile strength Yield	ASTM D638	65.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	2150 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	2100 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	125 °C
Vicat softening temperature	Vicat softening temperature	ASTM D152511	160 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	154 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	155 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	6E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	6E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	6E-05 cm/cm/°C
specific heat	specific heat	ASTMC351	1250 J/kg/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	142 °C
thermal conductivity	thermal conductivity	ASTMC177	0.21 W/m/K

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate 24hr	ASTM D570	0.16 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.16 %
melt mass-flow rate	melt mass-flow rate 330°C/2.16kg	ASTM D1238	30 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 330°C/2.16kg	ISO 1133	29.0 cm³/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.60to0.80 %
Specific volume	Specific volume	ASTM D792	0.830 cm³/g
density	density	ASTM D792	1.19 g/cm³
density	density	density	ISO 1183	1.20 g/cm³
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ASTM D1238	6.0 g/10min
density	density	ASTM D792	1.20 g/cm³
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.35 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 60Hz	ASTM D150	1.2E-03
	Dissipation factor	Dissipation factor 100Hz	ASTM D150	0.024
	Dissipation factor	Dissipation factor	Dissipation factor 50Hz	ASTM D150	1.2E-03
Dielectric constant	Dielectric constant 1MHz	ASTM D150	3.00
	Dielectric constant	Dielectric constant 60Hz	ASTM D150	3.15
	Dielectric constant	Dielectric constant	Dielectric constant 50Hz	ASTM D150	3.15
Dielectric strength	Dielectric strength 3.20mm,inAir	ASTM D149	20 kV/mm
Volume resistivity	Volume resistivity	ASTM D257	>2.6E+17 ohms·cm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Sale	ASTM D785	122
Rockwell hardness	Rockwell hardness M-Sale	ASTM D785	85

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Sale

ASTM D785

122

Rockwell hardness

M-Sale

ASTM D785

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.