| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | 80 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | 90 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 0.40 mm | UL 94 | V-0 |
| UL flame retardant rating | UL flame retardant rating 0.8 mm | UL 94 | V-0 |
| UL flame retardant rating | UL flame retardant rating 1.6 mm | UL 94 | V-0 |
| UL flame retardant rating | UL flame retardant rating 3.2 mm | UL 94 | V-0 |
| Burning wire flammability index | Burning wire flammability index 0.8 mm | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | Burning wire flammability index 1.6 mm | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | Burning wire flammability index 3.2 mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 0.40 mm | IEC 60695-2-13 | 960 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 0.8 mm | IEC 60695-2-13 | 960 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 1.6 mm | IEC 60695-2-13 | 775 °C |
| Extreme Oxygen Index | Extreme Oxygen Index | ISO 4589-2 | 33 % |
| European Railways Certifications | European Railways Certifications R22 | EN 45545-2 | HL3 |
| European Railways Certifications | European Railways Certifications R23 | EN 45545-2 | HL3 |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| bending strength | bending strength 23°C | ISO 178 | 135 Mpa |
| bending strength | bending strength 23°C | ASTM D790 | 125 Mpa |
| Bending modulus | Bending modulus 23°C | ISO 178 | 3700 Mpa |
| Bending modulus | Bending modulus 23°C | ASTM D790 | 3800 Mpa |
| Tensile strain | Tensile strain Break, 23°C | ISO 527-2 | 12 % |
| tensile strength | tensile strength Break, 23°C | ISO 527-2/1A | 80.0 Mpa |
| tensile strength | tensile strength Yield, 23°C | ISO 527-2/1A | 85.0 Mpa |
| Tensile modulus | Tensile modulus 23°C | ISO 527-2/1A | 3800 Mpa |
| injection | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| drying temperature | drying temperature | 80 °C | |
| Suggested maximum moisture content | Suggested maximum moisture content | 0.20 % | |
| Temperature at the rear of the barrel | Temperature at the rear of the barrel | 260 to 270 °C | |
| Temperature in the middle of the barrel | Temperature in the middle of the barrel | 265 to 275 °C | |
| Temperature at the front of the material cylinder | Temperature at the front of the material cylinder | 265 to 275 °C | |
| Mold temperature | Mold temperature | 60 to 80 °C |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 1.8 MPa, Unannealed | ISO 75-2/Af | 85.0 °C |
| Hot deformation temperature | Hot deformation temperature 0.45 MPa, Unannealed | ISO 75-2/Bf | 237 °C |
| Melting temperature | Melting temperature | ISO 11357-3 | 263 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Outdoor applicability | Outdoor applicability | UL 746C | f1 |
| Water absorption rate | Water absorption rate Equilibrium, 23°C, 50% RH | ISO 62 | 2.7 % |
| Water absorption rate | Water absorption rate 24 hr, 23°C | ISO 62 | 0.88 % |
| Shrinkage rate | Shrinkage rate Flow | ISO 294-4 | 1.5 % |
| Shrinkage rate | Shrinkage rate 横向Flow | ISO 294-4 | 1.3 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Compared to the anti leakage trace index | Compared to the anti leakage trace index Solution A | IEC 60112 | PLC 0 |
| Dissipation factor | Dissipation factor | IEC 60250 | 0.017 |
| Relative permittivity | Relative permittivity | IEC 60250 | 3.50 |
| Dielectric strength | Dielectric strength 2.00 mm | IEC 60243-1 | 21 KV/mm |
| Dielectric strength | Dielectric strength 0.800 mm | IEC 60243-1 | 33 KV/mm |
| Volume resistivity | Volume resistivity | IEC 60093 | 3.0E+15 ohms·cm |
| Surface resistivity | Surface resistivity | IEC 60093 | 3.0E+15 ohms |