mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus 23℃	ISO 527-2	2300 Mpa
Rockwell hardness	Rockwell hardness 23℃	ISO 2039-2	105 R scale
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃	ISO 179	15.0 KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30℃	ISO 179	5.00 KJ/m
bending strength	bending strength 23℃	ISO 178	67.0 Mpa
Bending modulus	Bending modulus 23℃	ISO 178	2450 Mpa
Tensile stress	Tensile stress 23℃，Yield	ISO 527-2	39.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 2.50mm	UL 94	5VA
	UL flame retardant rating	UL flame retardant rating 2.20mm	UL 94	5VB
	UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.50mm	UL 94	V-0
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ISO 11359-2	0.000080 cm/cm/℃
Hot deformation temperature	Hot deformation temperature 1.80MPa，Unannealed	ISO 75-2/Af	74.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate Flow,23℃	ISO 294-4	0.40-0.60 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

Flow,23℃

ISO 294-4

0.40-0.60 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.