PBT XENOY™ 6620U resin SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	72 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	670 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	900 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	51 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	54 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D4812	1600 J/m
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	56.3 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.5mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	63.6 MPa
tensile strength	tensile strength Yield	ISO 527-2/50	41.1 MPa
	tensile strength	tensile strength Break	ASTM D638	32.9 MPa
	tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	31.7 MPa
elongation	elongation Yield	ASTM D638	4.2 %
Tensile strain	Tensile strain Yield	ISO 527-2/50	3.9 %
elongation	elongation Break	ASTM D638	150 %
Tensile strain	Tensile strain Break	ISO 527-2/50	19 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	1780 MPa
Bending modulus	Bending modulus	Bending modulus	ISO 178	1700 MPa
bending strength	bending strength	ISO 178	60.0 MPa
Tensile modulus	Tensile modulus	ASTM D638	1780 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	1830 MPa
tensile strength	tensile strength Yield	ASTM D638	43.7 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	98.9 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	60.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	9.9E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	1E-04 cm/cm/°C
RTI Elec	RTI Elec	UL 746	75.0 °C
RTI Imp	RTI Imp	UL 746	75.0 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	50.5 °C
Vicat softening temperature	Vicat softening temperature	ASTM D152510	123 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	119 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	122 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	9.9E-05 cm/cm/°C
RTI Str	RTI Str	UL 746	75.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Specific volume	Specific volume	ASTM D792	0.835 cm³/g
density	density	ISO 1183	1.21 g/cm³
melt mass-flow rate	melt mass-flow rate 266°C/5.0kg	ASTM D1238	22 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 265°C/5.0kg	ISO 1133	17.1 cm³/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	1.6to1.8 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD：3.20mm	Internal Method	1.6to1.8 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.14 %
density	density	ASTM D792	1.20 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Arc resistance	Arc resistance	ASTM D495	PLC 5
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 0
High arc combustion index	High arc combustion index HAI	UL 746	PLC 0
High voltage arc tracing rate	High voltage arc tracing rate HVTR	UL 746	PLC 1
Hot wire ignition	Hot wire ignition HWI	UL 746	PLC 3

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.