AES+PC+AS(SAN) LNP™ LUBRICOMP™ Lexan_WR6300 compound SABIC

So sánh

Bảng thông số kỹ thuật

	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature	ASTM D15255	137 °C
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/2.16kg	ISO 1133	38.0 cm³/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.50to0.70 %
tensile strength	tensile strength Yield	ASTM D638	60.7 MPa
tensile strength	tensile strength	tensile strength Break	ASTM D638	61.4 MPa
elongation	elongation Break	ASTM D638	160 %
density	density	ASTM D792	1.17 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/2.16kg	ISO 1133	38.0 cm³/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.50to0.70 %
tensile strength	tensile strength Yield	ASTM D638	60.7 MPa
tensile strength	tensile strength	tensile strength Break	ASTM D638	61.4 MPa
elongation	elongation Break	ASTM D638	160 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2490 MPa
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	96.5 MPa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	170 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	680 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ASTM D4812	2500 J/m
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	60.2 J
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	134 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	117 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	121 °C
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	680 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D4812	2500 J/m
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	60.2 J
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	134 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	117 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	121 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15254	137 °C
RTI Elec	RTI Elec	UL 746	80.0 °C
RTI Imp	RTI Imp	UL 746	80.0 °C
RTI	RTI	UL 746	80.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	1.2E-04 cm/cm/°C
RTI Elec	RTI Elec	UL 746	80.0 °C
RTI Imp	RTI Imp	UL 746	80.0 °C
RTI Str	RTI Str	UL 746	80.0 °C
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2490 MPa
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	96.5 MPa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	170 J/m
UL flame retardant rating	UL flame retardant rating 1.50mm	UL 94	HB
density	density	ASTM D792	1.17 g/cm³
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to40°C	ASTME831	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to40°C	ASTME831	1.2E-04 cm/cm/°C

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.