PA12 VESTAMID® Care ML21 Altuglas International of Arkema Inc.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C,Complete Break	ISO 179/1eA	9.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C,Complete Break	ISO 179/1eA	32 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.6mm

UL 94

UL flame retardant rating

3.2mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Nominal tensile fracture strain	Nominal tensile fracture strain 23°C	ISO 527-2/50	>50 %
Tensile strain	Tensile strain Yield,23°C	ISO 527-2/50	5.0 %
tensile strength	tensile strength Yield,23°C	ISO 527-2/50	45.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2	1400 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	1.5E-04 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357	178 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B	140 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/A	170 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	50.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	110 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Stickiness	Stickiness	ISO 307	230 cm³/g
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.80 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	1.6 %
Shrinkage rate	Shrinkage rate MD:2.00mm	ISO 294-4	0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD:2.00mm	ISO 294-4	1.3 %
density	density 23°C	ISO 1183	1.01 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.