impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	25 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	35 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	20 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	HB
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	650 °C
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	23 %
BurningBehavior	BurningBehavior	ISO 3795	passed

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	6300 Mpa
tensile strength	tensile strength Break,23°C	ASTM D638	117 Mpa
tensile strength	tensile strength	tensile strength Break,23°C	ISO 527-2/5	120 Mpa
elongation	elongation Break,23°C	ASTM D638	3.0 %
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	3.0 %
Bending modulus	Bending modulus 23°C	ASTM D790	5700 Mpa
Bending modulus	Bending modulus	Bending modulus 23°C	ISO 178/A	5700 Mpa
bending strength	bending strength 23°C	ASTM D790	185 Mpa
	bending strength	bending strength 3.5%Strain	ISO 178/A	-- Mpa
		bending strength	bending strength 23°C	ISO 178	185 Mpa
		bending strength	bending strength	bending strength FlexuralStrainatFlexuralStrength5(23°C)		4.0 %
Tensile modulus	Tensile modulus 23°C	ASTM D638	6310 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	210 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	180 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to55°C	ISO 11359-2	8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	3E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 8.0MPa,Unannealed	ISO 75-2/C	55.0 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	200 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	200 °C
Melting temperature	Melting temperature	ISO 11357-3	218 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	2.6 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	7.8 %
Shrinkage rate	Shrinkage rate MD:120°C,2hr,3.00mm3	ISO 2577	0.10 %
	Shrinkage rate	Shrinkage rate MD:280°C,3.00mm2	ISO 2577	0.34 %
		Shrinkage rate	Shrinkage rate TD:120°C,2hr,3.00mm3	ISO 294-4	0.21 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate TD:280°C,3.00mm2	ISO 2577	0.67 %
Apparent density	Apparent density	ISO 60	0.70 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 23°C,1MHz	IEC 60250	0.018
Dissipation factor	Dissipation factor	Dissipation factor 23°C,100Hz	IEC 60250	8E-03
Relative permittivity	Relative permittivity 23°C,1MHz	IEC 60250	3.70
Relative permittivity	Relative permittivity	Relative permittivity 23°C,100Hz	IEC 60250	4.10
Surface resistivity	Surface resistivity	IEC 60093	1E+15 ohms
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 2
Dielectric strength	Dielectric strength 23°C,1.00mm	IEC 60243-1	30 KV/mm
Volume resistivity	Volume resistivity 23°C	IEC 60093	1E+13 ohms·cm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	190 Mpa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

190 Mpa

film	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Thin film puncture strength	Thin film puncture strength --7	ISO 6603-2	560 N
	Thin film puncture strength	Thin film puncture strength --6	ISO 6603-2	505 N
		Thin film puncture strength	Thin film puncture strength --7	ISO 6603-2	2.00 J
		Thin film puncture strength	Thin film puncture strength	Thin film puncture strength --6	ISO 6603-2	1.50 J

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ISO Shortcut	ISO Shortcut	ISO 1874	PA6/66.GHR.14-060.GF15

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ISO Shortcut

ISO 1874

PA6/66.GHR.14-060.GF15

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.