PA66 Zytel® 103HSL DUPONT USA

Đặc tính:
Chống va đập cao
Ổn định nhiệt
Lĩnh vực ứng dụng:
Ứng dụng điện
Thiết bị gia dụng nhỏ
Giấy chứng nhận:
UL
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	5.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	4.5 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	400kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180/1A	5.5 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	6.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	5.0 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	300kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	NoBreak

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.71mm	UL 94	V-2
	UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating 0.71mm	IEC 60695-11-10,-20	V-2
		UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.5mm	IEC 60695-11-10,-20	V-2
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	28 %
FMVSS flammability	FMVSS flammability	FMVSS302	SE

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2	3100 Mpa
tensile strength	tensile strength Yield	ISO 527-2	85.0 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2	4.5 %
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2	20 %
Tensile creep modulus	Tensile creep modulus 1hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	Tensile creep modulus 1000hr	ISO 899-1	-- Mpa
Bending modulus	Bending modulus	ISO 178	2800 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	240 °C
Melting temperature	Melting temperature	ISO 11357-3	262 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	1.1E-04 cm/cm/°C
Effective thermal diffusivity coefficient	Effective thermal diffusivity coefficient		5E-08 m²/s
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	200 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	70.0 °C
Glass transition temperature	Glass transition temperature	ISO 11357-2	60.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Stickiness	Stickiness	ISO 307	145 cm³/g
density	density	ISO 1183	1.14 g/cm³
Shrinkage rate	Shrinkage rate TD	ISO 294-4	1.3 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	1.3 %
Water absorption rate	Water absorption rate Saturation,23°C,2.00mm	ISO 62	8.5 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,2.00mm,50%RH	ISO 62	2.6 %
MediumDensity	MediumDensity		0.980 g/cm³
Top out temperature	Top out temperature		190 °C
SpecificHeatCapacity of Melt	SpecificHeatCapacity of Melt		2790 J/kg/°C
ThermalConductivityofMelt	ThermalConductivityofMelt		0.16 W/m/K

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohms·cm
Dielectric strength	Dielectric strength	IEC 60243-1	31 KV/mm
Relative permittivity	Relative permittivity 100Hz	IEC 60250	3.80
Relative permittivity	Relative permittivity	Relative permittivity 1MHz	IEC 60250	3.50
Dissipation factor	Dissipation factor 100Hz	IEC 60250	7.5E-03
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.017
Compared to the anti leakage trace index	Compared to the anti leakage trace index 3.00mm	UL 746	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 0

film	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Yield，MD	ISO 527-3	4.5 %

film

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Tensile strain

Yield，MD

ISO 527-3

4.5 %

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
EmissionofOrganicCompounds	EmissionofOrganicCompounds	VDA277	2.10 µgC/g
Odor	Odor	VDA270	2.50

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

EmissionofOrganicCompounds

VDA277

2.10 µgC/g

Odor

VDA270

2.50

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.