thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ASTM D696	1.2E-04 cm/cm/°C
Crystallization peak temperature	Crystallization peak temperature DSC	Internal Method	112 °C
Melting temperature	Melting temperature	Internal Method	135 °C
Vicat softening temperature	Vicat softening temperature	ASTM D1525	125 °C
Brittle temperature	Brittle temperature	ASTM D746	<-100 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	70.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 190°C/21.6kg	ASTM D1238	29 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 190°C/2.16kg	ASTM D1238	0.40 g/10min
density	density	ASTM D792	0.954 g/cm³
Environmental stress cracking resistance	Environmental stress cracking resistance F50	ASTM D1693B	50.0 hr

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
TopCrushingLoadatFailure	TopCrushingLoadatFailure 23°C	ASTM D2659	50000 g

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

TopCrushingLoadatFailure

23°C

ASTM D2659

50000 g

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.