PPO(PPE)+PS+PP NORYL™ WCV072 resin SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	67 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	34 kJ/m²
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	45.9 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	37 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	6.9 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	310 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	53.2 MPa
bending strength	bending strength	bending strength	ISO 178	59.3 MPa
Bending modulus	Bending modulus	ISO 178	1750 MPa
Bending modulus	Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	1560 MPa
Tensile strain	Tensile strain Break	ISO 527-2/50	46 %
elongation	elongation Break	ASTM D638	83 %
Tensile strain	Tensile strain Yield	ISO 527-2/50	11 %
elongation	elongation Yield	ASTM D638	15 %
tensile strength	tensile strength Break	ISO 527-2/50	42.1 MPa
tensile strength	tensile strength	tensile strength Break	ASTM D638	41.5 MPa
Tensile modulus	Tensile modulus	ASTM D638	1710 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	1760 MPa
tensile strength	tensile strength Yield	ASTM D638	43.8 MPa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	44.6 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	114 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature	ASTM D152510	114 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	98.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	92.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	1.1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	1.1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	8.4E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	8.5E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	117 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.03 g/cm³
density	density	density	ISO 1183	1.03 g/cm³
melt mass-flow rate	melt mass-flow rate 280°C/5.0kg	ASTM D1238	14 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/5.0kg	ISO 1133	13.4 cm³/10min
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.12 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.050 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.