PC XANTAR® C MC 3652 Mitsubishi Chemical Corporation

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	45 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	50 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/4A	65 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C	ISO 180/4A	55 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180/4A	50 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NoBreak

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	22 %

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Extreme Oxygen Index

ISO 4589-2

22 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	80.0 MPa
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2	>50 %
Tensile strain	Tensile strain Yield	ISO 527-2	4.0 %
tensile strength	tensile strength Yield	ISO 527-2	50.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2	2200 MPa
Bending modulus	Bending modulus	ISO 178	2300 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	108 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	7E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	123 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.60 %
Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.60 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 260°C/5.0kg	ISO 1133	18.0 cm³/10min
density	density	ISO 1183	1.12 g/cm³
ThermalConductivityofMelt	ThermalConductivityofMelt		0.23 W/m/K

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	>1.0E+15 ohms

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

IEC 60093

>1.0E+15 ohms·cm

Surface resistivity

IEC 60093

>1.0E+15 ohms

film	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Thin film puncture strength	Thin film puncture strength --4	ISO 6603-2	65.0 J
Thin film puncture strength	Thin film puncture strength --3	ISO 6603-2	55.0 J
Thin film puncture strength	Thin film puncture strength --2	Internal Method	55.0 J

film

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Thin film puncture strength

--4

ISO 6603-2

65.0 J

Thin film puncture strength

--3

ISO 6603-2

55.0 J

Thin film puncture strength

--2

Internal Method

55.0 J

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.