| Particle size distribution | Particle size distribution | Internal Method | >98.0 % |
| tensile strength | tensile strength Break3 | Internal Method | >33.0 MPa |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap --3 | Internal Method | >110 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap --2 | Internal Method | >90 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength | Internal Method | 无断裂 |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | Internal Method | >80.0 °C |
| density | density | Internal Method | 0.935to0.940 g/cm³ |
| Apparent density | Apparent density --2 | Internal Method | >0.35 g/cm³ |
| Apparent density | Apparent density --3 | Internal Method | >0.38 g/cm³ |
| molecular weight distribution | molecular weight distribution | Internal Method | 1000000to2000000 |
| Volatile compounds | Volatile compounds | Internal Method | <0.15 wt% |
| tensile strength | tensile strength Break2 | Internal Method | >32.0 MPa |
| Tensile strain | Tensile strain Break3 | Internal Method | 400 % |
| Tensile strain | Tensile strain Break2 | Internal Method | 350 % |