PA6 TAROMID B 280 G3 Taro Plast S.p.A.
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179 | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -20°C | ISO 179 | 25 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179 | 32 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C,3.20mm | ASTMD256 | 60 J/m |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 1.0mm | UL 94 | HB |
| Hot filament ignition temperature | Hot filament ignition temperature 2.0mm | IEC 60695-2-13 | 750 °C |
| Extreme Oxygen Index | Extreme Oxygen Index | ASTM D2863 | 24 % |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus | ASTMD638 | 6100 MPa |
| tensile strength | tensile strength Break | ASTMD638 | 125 MPa |
| elongation | elongation Break | ASTMD638 | 4.0 % |
| Bending modulus | Bending modulus | ASTMD790 | 5800 MPa |
| bending strength | bending strength -- | ISO 178 | 150 MPa |
| bending strength | bending strength Break | ASTM D790 | 150 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Continuous use temperature | Continuous use temperature --6 | IEC 60216 | 180 °C |
| Vicat softening temperature | Vicat softening temperature -- | ASTMD15257 | 210 °C |
| Vicat softening temperature | Vicat softening temperature -- | ASTMD15258 | 205 °C |
| Melting temperature | Melting temperature | ASTMD211 | 222 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：-30to30°C | ASTM D696 | 4E-05 cm/cm/°C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ASTMD648 | 190 °C |
| Continuous use temperature | Continuous use temperature --3 | IEC 60216 | 90.0 °C |
| Continuous use temperature | Continuous use temperature --4 | IEC 60216 | 130 °C |
| Continuous use temperature | Continuous use temperature --5 | IEC 60216 | 140 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| GranuleHumidity | GranuleHumidity | Internal Method | <0.15 % |
| density | density | ASTMD792 | 1.19to1.21 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 250°C/2.16kg | ASTMD1238 | 15 g/10min |
| Shrinkage rate | Shrinkage rate MD | ASTM D955 | 0.40to0.50 % |
| Shrinkage rate | Shrinkage rate TD | ASTM D955 | 0.80to1.0 % |
| Water absorption rate | Water absorption rate 23°C,24hr | ASTMD570 | 1.1 % |
| Water absorption rate | Water absorption rate Saturation | ASTM D570 | 7.0 % |
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 7.0 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Volume resistivity | Volume resistivity | ASTM D257 | 7E+15 ohms·cm |
| Dielectric strength | Dielectric strength 2.00mm | ASTM D149 | 22 kV/mm |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index SolutionA | IEC 60112 | PLC 1 |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Rockwell hardness | Rockwell hardness R-Scale | ASTM D785 | 118 |