PPO NORYL™ SE1GFN2-701 SABIC INNOVATIVE SHANGHAI

112

Đặc tính:
Tăng cường
Gia cố sợi thủy tinh
Lĩnh vực ứng dụng:
Phụ kiện truyền thông điệ
Phụ kiện truyền thông điệ
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ASTM D4812	520 J/m
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C8	ISO 180/1U	27 kJ/m²
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C8	ISO 180/1U	28 kJ/m²
Dart impact	Dart impact 23°C, Total Energy	ASTM D3763	18.0 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5 mm	UL 94	V-1

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.5 mm

UL 94

V-1

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus --3	ASTM D638	7100 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	6400 Mpa
tensile strength	tensile strength Break4	ASTM D638	120 Mpa
tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	100 Mpa
elongation	elongation Break4	ASTM D638	3.0 %
elongation	elongation	elongation Break	ISO 527-2/50	2.5 %
Bending modulus	Bending modulus 50.0 mm Span5	ASTM D790	5500 Mpa
Bending modulus	Bending modulus	Bending modulus --6	ISO 178	5600 Mpa
bending strength	bending strength --6,7	ISO 178	150 Mpa
bending strength	bending strength	bending strength Yield, 50.0 mm Span5	ASTM D790	140 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	110 to 120 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Suggested injection volume	Suggested injection volume	30 to 70 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	265 to 315 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	275 to 320 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	290 to 325 °C
Spray nozzle temperature	Spray nozzle temperature	300 to 325 °C
Processing (melt) temperature	Processing (melt) temperature	300 to 325 °C
Mold temperature	Mold temperature	80 to 110 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	20 to 100 rpm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 3.20 mm	ASTM D648	142 °C
	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	134 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	133 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D15259	142 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	144 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ASTM E831	2.5E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ISO 11359-2	3.0E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40°C	ISO 11359-2	7.5E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 280°C/5.0 kg	ASTM D1238	3.5 g/10 min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/5.0 kg	ISO 1133	3.00 cm3/10min
Shrinkage rate	Shrinkage rate 3.20 mm，Flow	Internal Method	0.20 - 0.50 %
Water absorption rate	Water absorption rate 24 hr, 23°C	ISO 62	0.11 %
Water absorption rate	Water absorption rate	Water absorption rate 24 hr, 23°C2	ISO 62	0.040 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	ASTM D257	1.3E+17 ohms
Volume resistivity	Volume resistivity	ASTM D257	2.0E+16 ohms·cm
Dielectric strength	Dielectric strength 1.60 mm, in Oil	ASTM D149	26 KV/mm
Dielectric strength	Dielectric strength	Dielectric strength 1.50 mm, in Oil	IEC 60243-1	26 KV/mm
Dielectric constant	Dielectric constant 1 MHz	ASTM D150	2.93
Dielectric constant	Dielectric constant	Dielectric constant 1 MHz	IEC 60250	2.90
Dissipation factor	Dissipation factor 1 MHz	ASTM D150	3.4E-3

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.