PA6 Ultramid® B3WG6 BASF GERMANY

215

Đặc tính:
Ổn định nhiệtChống dầuĐóng gói: Gia cố sợi thủy30%Đóng gói theo trọng lượng
Lĩnh vực ứng dụng:
Lĩnh vực ô tôPhụ tùng mui xeỨng dụng trong lĩnh vực ô
Giấy chứng nhận:
UL
So sánh Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179	9.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	12 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179	65 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	80 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ASTM D256	110 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	150 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180	12 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus 23°C	ISO 527-2	9500 Mpa
tensile strength	tensile strength Break,23°C	ASTM D638	180 Mpa
tensile strength	tensile strength	tensile strength Break,23°C	ISO 527-2	180 Mpa
Tensile strain	Tensile strain Break,23°C	ISO 527-2	3.0 %
Bending modulus	Bending modulus 23°C	ISO 178	8300 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	220 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	220 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	210 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	205 °C
Melting temperature	Melting temperature	ASTM D3418	220 °C
Melting temperature	Melting temperature	Melting temperature	ISO 3146	220 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.36 g/cm³
density	density	density	ISO 1183	1.36 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 275°C/5.0kg	ISO 1133	40.0 cm3/10min
Shrinkage rate	Shrinkage rate MD：3.18mm		0.30 %
Water absorption rate	Water absorption rate Saturation	ASTM D570	6.6 %
	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	6.6 %
		Water absorption rate	Water absorption rate Equilibrium,50%RH	ASTM D570	2.1 %
		Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	2.1 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.