impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 0°C	ISO 180/1A	30 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	41 kJ/m²
Dart impact	Dart impact -30°C,EnergyatPeakLoad	ASTM D3763	24.0 J
Dart impact	Dart impact	Dart impact 23°C,EnergyatPeakLoad	ASTM D3763	22.0 J
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C3	ISO 179/1eA	6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C4	ISO 179/1eA	34 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1	1650 MPa
tensile strength	tensile strength Yield	ISO 527-2/50	19.0 MPa
tensile strength	tensile strength	tensile strength Break	ISO 527-2/1A/50	13.0 MPa
Tensile strain	Tensile strain Break	ISO 527-2/50	100 %
Bending modulus	Bending modulus 64.0mmSpan	ISO 178	1760 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	100 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	53.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to100°C	ISO 11359-2	4.9E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-30to100°C	ISO 11359-2	1.3E-04 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate MD:80°C,1hr	Internal Method	0.60 %
	Shrinkage rate	Shrinkage rate MD:120°C,30分钟	Internal Method	0.71 %
	Shrinkage rate	Shrinkage rate	Shrinkage rate MD:23°C,48hr	Internal Method	0.55 %
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	34 g/10min
Shrinkage rate	Shrinkage rate TD:80°C,1hr	Internal Method	1.1 %
	Shrinkage rate	Shrinkage rate TD:120°C,30分钟	Internal Method	1.1 %
	Shrinkage rate	Shrinkage rate	Shrinkage rate TD:23°C,48hr	Internal Method	0.95 %
density	density	ASTM D792	0.968 g/cm³
density	density	density	ISO 1183	0.960 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.