mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 1/4〃带Notched	ASTM D-256	105 J/m
Bending modulus	Bending modulus	ASTM D-790	2180 Mpa
bending strength	bending strength	ASTM D-790	69 Mpa
tensile strength	tensile strength	ASTM D-638	42 Mpa
Rockwell hardness	Rockwell hardness	ASTM D-785	42 M
tensile strength	tensile strength	ASTM D638/ISO 527	47 kg/cm²(MPa)[Lb/in²]
Bending modulus	Bending modulus	ASTM D790/ISO 178	2300 kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	ASTM D790/ISO 178	71 kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength	Charpy Notched Impact Strength	ASTM D256/ISO 179	98 kg·cm/cm(J/M)ft·lb/in

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Combustibility	Combustibility	UL 94	1.5mmHB
Vicat softening temperature	Vicat softening temperature 50N	ASTM D-1525	86 °C
Hot deformation temperature	Hot deformation temperature 6.4mm,1.82MPa	ASTM D-648	72 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Combustibility

UL 94

1.5mmHB

Vicat softening temperature

50N

ASTM D-1525

86 °C

Hot deformation temperature

6.4mm,1.82MPa

ASTM D-648

72 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate 2mm		0.3-0.5 %
turbidity	turbidity 2mm	ASTM D-1003	2.5 %
Total Light Transmittance	Total Light Transmittance 2mm	ASTM D-1003	91 %
melt mass-flow rate	melt mass-flow rate	ASTM D1238/ISO 1133	5.5 g/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.