| Tensile stress change rate | Tensile stress change rate 135°C,168hr，Break | IEC 60811-1-2 | -15 % |
| Smoke density | Smoke density | ASTM D2843 | <3.5 % |
| HalogenAcidGasEvolution | HalogenAcidGasEvolution | IEC 60754-1 | <0.50 % |
| compressive strength | compressive strength 100°C，K值 | IEC 60811-2-1 | 40 % |
| Cold bend | Cold bend -30°C | IEC 60811-1-4 | pass |
| thermosetting | thermosetting Elongationunderload,20N/cm2:200°C | IEC 60811-2-1 | 30 % |
| thermosetting | thermosetting Permanentelongationaftercooling | IEC 60811-2-1 | 0.0 % |
| Temperature index | Temperature index | ISO 4589-3 | >300 °C |
| Dielectric constant | Dielectric constant 20°C，Ki | IEC 60502 | 1.3E+12 ohms·cm |
| Dielectric constant | Dielectric constant 90°C，Ki | IEC 60502 | 2.9E+08 ohms·cm |
| Conductivity of gases | Conductivity of gases | IEC 60754-2 | 13.0 µS/cm |
| Extreme Oxygen Index | Extreme Oxygen Index | ISO 4589-2 | 36 % |
| Corrosion of flue gas | Corrosion of flue gas pH | IEC 60754-2 | 4.60 |
| density | density | BS2782620A | 1.51 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 190°C/2.16kg | Internal Method | 7.5 g/10min |
| tensile strength | tensile strength | IEC 60811-1-1 | 14.0 MPa |
| Tensile strain | Tensile strain Break | IEC 60811-1-1 | 150 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 70°C,72hr,在ASTM#2油中 | | -47 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 100°C,24hr,在ASTM#2油中 | | -58 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 135°C,168hr | IEC 60811-1-2 | 20 % |
| Tensile stress change rate | Tensile stress change rate 70°C,72hr,在ASTM#2油中，Break | | 3.0 % |
| Tensile stress change rate | Tensile stress change rate 100°C,24hr,在ASTM#2油中，Break | | -20 % |