PA46 Stanyl® TW300 DSM JAPAN

319

Đặc tính:
Ổn định nhiệt
Lĩnh vực ứng dụng:
Ứng dụng ô tô
Bộ phận gia dụng
So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	4.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180/1A	4.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	10 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Flammability level	Flammability level	UL 94	V-2
Flammability level	Flammability level	UL 94	V-2

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Flammability level

UL 94

V-2

Flammability level

UL 94

V-2

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus 160°C	ISO 178	600 Mpa
	Bending modulus	Bending modulus 120°C	ISO 178	800 Mpa
	Bending modulus	Bending modulus	Bending modulus --	ISO 178	3000 Mpa
Nominal tensile fracture strain	Nominal tensile fracture strain 200°C	ISO 527-2	> 50 %
	Nominal tensile fracture strain	Nominal tensile fracture strain 180°C	ISO 527-2	> 50 %
		Nominal tensile fracture strain	Nominal tensile fracture strain 160°C	ISO 527-2	> 50 %
			Nominal tensile fracture strain	Nominal tensile fracture strain 120°C	ISO 527-2	> 50 %
			Nominal tensile fracture strain	Nominal tensile fracture strain	Nominal tensile fracture strain --	ISO 527-2	40 %
tensile strength	tensile strength Yield, 200°C	ISO 527-2	30.0 Mpa
	tensile strength	tensile strength Yield, 180°C	ISO 527-2	35.0 Mpa
		tensile strength	tensile strength Yield, 160°C	ISO 527-2	40.0 Mpa
			tensile strength	tensile strength Yield, 120°C	ISO 527-2	50.0 Mpa
			tensile strength	tensile strength	tensile strength Yield	ISO 527-2	100 Mpa
Tensile modulus	Tensile modulus 200°C	ISO 527-2	500 Mpa
	Tensile modulus	Tensile modulus 180°C	ISO 527-2	600 Mpa
		Tensile modulus	Tensile modulus 160°C	ISO 527-2	650 Mpa
			Tensile modulus	Tensile modulus 120°C	ISO 527-2	800 Mpa
			Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2	3300 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed	ISO 75-2/B	280 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed	ISO 75-2/A	190 °C
Melting temperature	Melting temperature	ISO 11357-3	295 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ISO 11359-2	8.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow	ISO 11359-2	1.1E-4 cm/cm/°C
RTI Elec	RTI Elec 0.75 mm	UL 746	150 °C
Thermal Index - 5000 hr	Thermal Index - 5000 hr	IEC 60216	152 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	3.7 %
Shrinkage rate	Shrinkage rate Flow	ISO 294-4	2.0 %
Shrinkage rate	Shrinkage rate	Shrinkage rate 横向Flow	ISO 294-4	2.0 %
density	density	ISO 1183	1.18 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	1.0E+15 ohms·cm
Dielectric strength	Dielectric strength	IEC 60243-1	25 KV/mm
Relative permittivity	Relative permittivity 100 Hz	IEC 60250	3.90
Relative permittivity	Relative permittivity	Relative permittivity 1 MHz	IEC 60250	3.60
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 1

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.